Page 2 of 3
Results 25 - 48 of 53

G-4786

Palm Wax

Property Method Typical
Melting Point F/C AOCS Cc 1-25 135.7 / 57.6

G-4787

Palm Wax

Property Method Typical
Melting Point F/C AOCS Cc 1-25 134.6 / 57

G-4788

Palm Wax

Property Method Typical
Melting Point F/C AOCS Cc 1-25 132.8 / 56

G-4789

Palm Wax

Property Method Typical
Melting Point F/C AOAC 920 156 118.4 / 48

G-4792

Palm Wax

Property Method Typical
Melting Point F/C AOAC 920 156 138.2 / 59

G-4793

Palm Wax

Property Method Typical
Melting Point F/C AOCS Cc 1-25 138.2 / 59

G-4794

Palm Wax

Property Method Typical
Melting Point F/C AOCS Cc 1-25 129.2 / 54

G-4795

Triple Pressed Stearic Acid

Property Method Typical

G-4796

Palm Wax

Property Method Typical
Melting Point F/C AOCS Cc 1-25 140 / 59

G-4797

Palm Wax

Property Method Typical
Melting Point F/C AOAC 920 156 134.6 / 57

G-4798

Palm Wax

Property Method Typical
Melting Point F/C AOAC 920 156 120.2 / 49

G-4799

Palm Wax

Property Method Typical
Melting Point F/C AOCS Cc 1-25 132.8 / 56

G-0162

Polymer additive

Property Method Typical

G-0690

Saturating Wax

Property Method Typical
Congealing Point F/C ASTM D-938 135 / 57.2

G-0695

Saturating Wax

Property Method Typical
Congealing Point F/C ASTM D-938 141 / 60.6

G-0183

Saturating Wax

Property Method Typical
Congealing Point F/C ASTM D-938 141 / 60.5

G-0644

White Slack Wax

Property Method Typical
Melting Point F/C ASTM D-87 131/55

G-0642

White Slack Wax

Property Method Typical
Melting Point F/C ASTM D-87 127.9 / 53.3

G-0646

Slack Wax

Property Method Typical
Congealing Point F/C ASTM D-938 177.8 / 81

G-0647

Slack Wax

Property Method Typical
Congealing Point F/C ASTM D-938 154 / 67.8

G-0648

Slack Wax

Property Method Typical
Congealing Point F/C ASTM D-938 154 / 67.8

G-0635B

Slack Wax

Property Method Typical
Congealing Point F/C ASTM D-938 129.2 / 54

G-1560B

Slack Wax

Property Method Typical
Melting Point F/C ASTM D-87 124.2 / 51.2

G-5770

Micro Pet

Property Method Typical
Melting Point F/C ASTM D-127 175/79